HRI EncapsulantsGel
OE -6450
Elastomers
OE-6520
Elastomers
OE-6550
Resins
OE-6635
Resins
OE-6636
Resins
OE-6630
Resins
OE-6631
Resins
OE-6665
Lens Resins
SR-7010
Mix Ratio 1:1 1:1 1:1 1:3 1:2 1:4 1:2 1:20 1:1
Viscosity ( Part A )   (mPa.s) 2,900 10,000 22,000 31,700 13,000 2,100 5,900 100 20,000
Viscosity ( Part B )   (mPa.s) 1,400 1,000 1,100 2,850 5,100 2,300 13,500 2,400 7,000
Viscosity ( Mixed )   (mPa.s) 1,800 2,000 4,000 5,000 7,650 2,500 7,150 2,200 14,000
Curing Condition 100℃/1hr 150℃/1hr 150℃/1hr 150℃/2hr 150℃/1hr 150℃/2hr 150℃/2hr 150℃/2hr < 1 min@170°C
Hardness Penetration 70 26 (JIS A) 62 (JIS A) 33 (shore D) 34 (shore D) 41 (shore D) 69 (shore A) 68 (shore D) 67 (shore D)
Reflective Index 1.54 1.54 1.54 1.54 1.54 1.53 1.54 1.53 1.53
Transmittance, % @ 450 nm, 1 mm 100 100 100 100 100 100 100 99.5 99
Storage Condition 25℃/12M 25℃/6M 25℃/12M 25℃/12M 25℃/16M 25℃/12M 25℃/12M 25℃/12M 25℃/9M
NRI Encapsulants Gels
JCR-6110
Gels
Q1-4939
Gels
OE-6250
Elastomers
JCR-6126
Elastomers
JCR-6101UP
Elastomers
JCR- 6122
Elastomers
OE- 6336
Elastomers
EG-6301
Die Attach Adhesive
OE-8001
Mix Ratio 10:1 10:1 1:1 10:1 One Part 1:1 1:1 1:1 One Part
Viscosity ( Part A )(mPa.s) 2,000 6,000 444 130,000 _ 360 950 2,900 _
Viscosity ( Part B )(mPa.s) 660 3,000 440 100 _ 310 2,100 4,100 _
Viscosit ( Mixed ) (mPa.s) 2,100 5,400 500 86,400 20,000 350 1,500 3,400 5,700
Curing Condition 150℃/1hr 125℃/0.5hr 80℃/1hr 150℃/1hr 70℃/1hr + 150℃/2hr 150℃/1hr 150℃/1hr 150℃/1hr 150℃/2hr or 170℃/1hr
Hardness Shore- Penetration 200 Penetration 55 Penetration 45 26 (JIS A) 35 (JIS A) 35 (JIS A) 65 (JIS A) 71 (JIS A) 60 (JIS D)
Reflective Index 1.42 1.41 1.41 1.41 1.398 1.40 1.41 1.41 _
Transmittance, % @ 450 nm, 1 mm 99 91.5 100 Translucent Translucent 99 98 97 91
Storage Condition 25℃/12M 25℃/6M 25℃/6M 25℃/9M -5℃/6M 25℃/6M 25℃/6M 25℃/6M -15℃/product label